Drizoro - Maxflex 900 polysulfide putty

Two-component putty based on polysulfide resin with high chemical resistance, which chemically reacts after mixing to make the material elastomeric. It is characterized by a low elasticity coefficient.

Features

• chemical polymerization process during application
• high chemical and mechanical resistance
• for permanent contact with water
• application on a dry substrate at a temperature of +5 C to +50 C
• very good adhesion to most used materials in
• can be used for vertical joints up to 30 mm wide, and for horizontal joints up to 40 mm

Application

• filling expansion joints non-drinking water tank: sewage treatment plant tanks, technological water tanks, fire protection tanks, etc.
• sealing tray gaps and safety tubs under tanks
• sealing concrete-brick connections
• sealing the channel in, irrigation ditches, siphon in sewerage, tight passages
• sealing connections immersed in water
• sealing joints of concrete surfaces
• filling expansion gaps in hydrotechnical and other civil engineering structures
• sealing heavy and light joints prefabricated element w

Technical data

• component A - appearance white and homogeneous, cream putty
• component B - appearance white and homogeneous, cream putty
• solids content 2 h and 110 C component A and B 100%
• characteristics of the mixed product - gray and homogeneous appearance, cream putty
• application at 23 C approx. 30 min
• range of application from +5 C to +50 C
• characteristics of the vulcanized product (28 days at 23 C and 55% humidity) - rubber-like appearance
• Shore A hardness 23 (according to DIN 53505)
• elasticity, NF P 88506 85%
• modulus of elasticity, 1005 0.18 MPa (according to DIN 53504)
• traction resistance 0.50 MPa (according to DIN 53504)
• elongation at break 450-550% (according to DIN 53504)
• movement of expansion joints during use 25%
• temperature resistance range during operation from -30 C to +80 C
• very good weather and UV resistance
• chemical resistance: water, soapy water, brine - excellent; inorganic, dilute acids and bases - very good; mineral oils, fats - very good; oils, fuels, hydrocarbons - very good
• consumption - 100 ml is needed to fill 1 running meter of a joint measuring 10 x 10 mm
• packaging 2.5 l bucket